低ヨウ素化学輸送法によるCuGa_xAl_1-xS_2混晶の成長とフォトルミネッセンス
http://hdl.handle.net/10649/323
http://hdl.handle.net/10649/323bfb24c4b-ab9a-4bed-9e98-4037b07cb78c
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
K5_7.pdf (557.6 kB)
|
|
| アイテムタイプ | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2011-02-15 | |||||
| タイトル | ||||||
| タイトル | 低ヨウ素化学輸送法によるCuGa_xAl_1-xS_2混晶の成長とフォトルミネッセンス | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | departmental bulletin paper | |||||
| 著者 |
稲垣, 積
× 稲垣, 積× 本多, 仁× 飯田, 誠之 |
|||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1060 | |||||
| 姓名 | イナガキ, ツモル | |||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1061 | |||||
| 姓名 | ホンダ, ヒトシ | |||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1062 | |||||
| 姓名 | イイダ, セイシ | |||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1063 | |||||
| 姓名 | Inagaki, Tsumoru | |||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1064 | |||||
| 姓名 | Honda, Hitoshi | |||||
| 著者別名 | ||||||
| 識別子Scheme | WEKO | |||||
| 識別子 | 1065 | |||||
| 姓名 | Iida, Seishi | |||||
| 著者所属 | ||||||
| 値 | 長岡技術科学大学 | |||||
| 著者所属 | ||||||
| 値 | 長岡技術科学大学 | |||||
| 著者所属 | ||||||
| 値 | 長岡技術科学大学 | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | CuGaxAl1-xS2 mixed alloy crystals have been prepared directly from constituent elements using iodine transport method. EPMA studies of these crystals showed that the real values of x are smaller than the expected values for the stoichiometric of the elements, i.e. preferential incorporation of Al. This tendency is larger for large x. EPMA studies also revealed that the deviation from the stoichiometry occurs for CuGaS2 (x=1) and CuAlS2 (x=0) crystals. Lattice constants obtained by X-ray diffraction showed a monotonic decrease with decreasing x. The main peak energy of the low temperature photoluminescence spectrum under N2 laser excitation also showed a monotonical increase with decreasing x. This peak is close to the expected band gap energy for a corresponding value. All these results show that CuGaxAl1-xS2 alloy crystals were successfully grown. The green photoluminescence (peak at near 550nm) at 77K of CuGaS2 crystals was shown to be a donor-acceptor pair emission. The relevant donor and acceptor binding energies are estimated to be 50meV and 300meV respectively, from the comparison of the themal quenching and excitation spectrum of the emission. | |||||
| 書誌情報 |
長岡技術科学大学研究報告 巻 5, p. 39-46, 発行日 1984-01-31 |
|||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 0388-5631 | |||||
| 書誌レコードID | ||||||
| 収録物識別子タイプ | NCID | |||||
| 収録物識別子 | AN00177120 | |||||
| 著者版フラグ | ||||||
| 出版タイプ | VoR | |||||
| 出版タイプResource | http://purl.org/coar/version/c_970fb48d4fbd8a85 | |||||
| その他のタイトル | ||||||
| その他のタイトル | Vapor phase transport growth and photoluminescence studies of CuGaxAl1-xS2 mixed alloy crystals | |||||
| 出版者 | ||||||
| 出版者 | 長岡技術科学大学 | |||||